14th Sep 2020, 6:32 pm | #1 |
Octode
Join Date: Jun 2013
Location: Fleet, Hampshire, UK
Posts: 1,764
|
Rust question
Is rust progressive? I.e once it has begun does it continue to spread and damage metal, even if it is no longer in the environment that caused the rust originally?
Apologies if this is a dumb question, I couldn’t find the answer by searching. I have a chassis that has a little bit of rust on it, along with some transformer frames and laminations. I wouldn’t say it was serious or deep, the set works and I’m not fussed on the visuals as it will be hidden away. But I wondered if I should do anything preventative before putting it back in the cabinet, I.e to stop it getting worse. It was stored in a damp environment for many years but is now in a dry heated home. |
14th Sep 2020, 6:39 pm | #2 |
Octode
Join Date: Jun 2018
Location: Essex, UK.
Posts: 1,307
|
Re: Rust question
I've personally never had it spread. I can't see how it would if it's in a warm and dry environment as any remaining moisture would've been driven out after several days? Though once there's rust, if untreated it's much easier for it to spread if given the chance to
'77 Last edited by 19Seventy7; 14th Sep 2020 at 6:51 pm. |
14th Sep 2020, 7:09 pm | #3 |
Heptode
Join Date: Feb 2006
Location: Marlborough, Wiltshire, UK.
Posts: 915
|
Re: Rust question
No, it won’t spread. It needs both oxygen (air) and water (liquid or vapour) to create the various iron oxides. Keep it dry as in low humidity, non-condensing and it will go into suspended animation !
|
14th Sep 2020, 8:51 pm | #4 |
Dekatron
Join Date: Aug 2016
Location: Colchester, Essex, UK.
Posts: 4,092
|
Re: Rust question
Agree with posts 2 and 3. The critical thing with rust is it's porous nature- this as we know, is the reason even a small amount can't be sealed under fresh paint, carrying as it does it's own temporary supply of oxygen and water.
Dave |
14th Sep 2020, 8:53 pm | #5 |
Dekatron
Join Date: Apr 2009
Location: Oxfordshire, UK.
Posts: 4,928
|
Re: Rust question
I notice that one the various repair and restoration shows which seem currently popular on TV that they very often leave things rusty, believing that this gives them character or a period feel.
However, one show decided to go down the route of applying some wax on a cloth, which may have dislodged any loose rust, but left a rusty surface. They felt that this improved the appearance and was an additional measure to deter further rusting, but I realise for that this may not be something you feel worthwhile in this case. The only other issue that might be worth thinking about is whether the existing rust might shed any particles which might find their way in to some place where they do no good? Of course, this could be a case of "if it ain't bust, don't fix it". I think I could be a "rustophobe"? B
__________________
Saturn V had 6 million pounds of fuel. It would take thirty thousand strong men to lift it an inch. |
14th Sep 2020, 10:22 pm | #6 |
Nonode
Join Date: May 2007
Location: Preston, Lancashire, UK.
Posts: 2,510
|
Re: Rust question
I can't see any justification for retaining rust to give something 'character' - wear and tear of in-service use is one thing, rust is usually caused by neglect and bad storage after something has fallen out of use.
Andy |
14th Sep 2020, 11:00 pm | #7 |
Octode
Join Date: Jun 2013
Location: Fleet, Hampshire, UK
Posts: 1,764
|
Re: Rust question
Great news, I can enjoy it in it’s rusty goodness
I’d suspected the rust would cease once it was in a dry environment. Strangely after all the kit I’ve been mucking about with over the years, this is the first significant bit of rust I’ve encountered, most chassis’ I work on are perfect The worst part was the rear socket panel (HMV 501), it had very deep rust and no paint on it. I removed 99% of the rust with a wire brush drill attachment, then sprayed it white. |
15th Sep 2020, 8:11 am | #8 |
Dekatron
Join Date: Jan 2005
Location: Oxford, UK.
Posts: 17,825
|
Re: Rust question
I once got hold of a 1930s wall phone which had lived in a very wet environment. The chassis was thick with rust.
I removed the components, attacked it with a wire brush in an electric drill to remove the loose and friable stuff, cleaned it off with white spirit to leave a smoothish rusty surface (rather than bare metal), then sprayed with Hammerite smooth finish direct-to-metal paint. It looks fine and has been entirely stable. Nick. |
15th Sep 2020, 9:28 am | #9 |
Heptode
Join Date: Jul 2014
Location: Boston, Lincolnshire, UK.
Posts: 995
|
Re: Rust question
Another method not mentioned yet would be one of the commercial Phosphoric acid based rust treatments. They also form a phosphate layer which protects the surface from further rusting. I guess it depends a lot on whether the part is to be visible, or will be covered or painted in some way.
Alan |
15th Sep 2020, 9:53 am | #10 |
Moderator
Join Date: Jan 2003
Location: Ipswich, Suffolk, IP4, UK.
Posts: 21,252
|
Re: Rust question
My experience has been that radios stored indoors don't rust unless they get damp for some reason, for example in a steamy kitchen or laundry room. If a rusty radio is brought into a dry environment no further rusting takes place once it's dried out.
Radios kept in a damp shed or garage will eventually rust even though steel parts may have been plated or painted from new.
__________________
Graham. Forum Moderator Reach for your meter before you reach for your soldering iron. |
15th Sep 2020, 12:40 pm | #11 |
Dekatron
Join Date: Aug 2016
Location: Colchester, Essex, UK.
Posts: 4,092
|
Re: Rust question
Phosphoric acid is ideal for small steel parts that can be thoroughly de-rusted then immersed- but as a brush on jelly for (pitted) steel panels it promises what it can't deliver unless all the rust is completely removed from those nasty deep pits- not easy unless they are mechanically ground out. (Of course these days we have the Dremel..)
Dave |
15th Sep 2020, 12:47 pm | #12 |
Diode
Join Date: Jan 2020
Location: Northwood, London, UK.
Posts: 5
|
Re: Rust question
I use 36% hydrochloric acid for de-rusting. Sounds drastic but very effective. Then dry thoroughly and spray with 3 in 1 or any proprietary anti-rust coating. Strangely HCL acid seems to escape by some form of osmosis, even from thoroughly sealed bottles and tools,etc left in the vicinity which will rust rapidly. I know this sounds weird BUT I was plagued by corrosion in my workshop for years and tried everything;de-humidifiers, better ventilation,constant temperature above 18 degrees Centigrade, etc. Eventually I removed the sealed HCL bottles outside after leaving one over 3 foot distance from some immaculate brand new chisels and chrome vanadium coated spanners which heaviy corroded after 4-5 days!
|
15th Sep 2020, 1:01 pm | #13 | |
Octode
Join Date: Jun 2013
Location: Fleet, Hampshire, UK
Posts: 1,764
|
Re: Rust question
Quote:
|
|
15th Sep 2020, 2:01 pm | #14 |
Dekatron
Join Date: Aug 2016
Location: Colchester, Essex, UK.
Posts: 4,092
|
Re: Rust question
Post No.12- I have experienced the same effect with Hydrochloric (Muriatic?) Acid.
The polythene bottle started to suffer little blisters, and a steel table leg nearby became heavily rusted. No puddles or obvious leakage, but it was still evidently producing vapour. It's a brilliant immersion de-ruster (although i add it to water to bring it down to around 16%,it works out more economic, slower and safer.) Ideally it would be stored in a glass bottle with a tough HDPE jacket (but i doubt such a bottle exists!) Needless to say it eats Aluminium for breakfast. Dave |
15th Sep 2020, 2:21 pm | #15 |
Heptode
Join Date: Jul 2014
Location: Boston, Lincolnshire, UK.
Posts: 995
|
Re: Rust question
Hydrochloric acid is essentially just Hydrogen Chloride (HCl), which is a gas at room temperature, dissolved in water. I would assume the plastic bottles it was stored in were to some extent porous to HCl, or had become so through degradation over the years.
We used to keep most strong acids in glass bottles, which were then indeed kept inside wide-mouthed, screw top, plastic containers, themselves stood in large spill trays, in a dedicated chemical storage cupboard... Alan |
15th Sep 2020, 2:33 pm | #16 |
Dekatron
Join Date: Nov 2003
Location: Heckmondwike, West Yorkshire, UK.
Posts: 9,640
|
Re: Rust question
|
15th Sep 2020, 3:48 pm | #17 |
Dekatron
Join Date: Sep 2005
Location: Seaford, East Sussex, UK.
Posts: 5,997
|
Re: Rust question
I always clean off loose rust and finish off with a light bicycle oil, not WD40 as it goes sticky although this was originally designed for this purpose. If it's rusting then the original plating has has been sacrificed.
|
15th Sep 2020, 4:44 pm | #18 |
Dekatron
Join Date: Sep 2011
Location: Rugeley, Staffordshire, UK.
Posts: 8,821
|
Re: Rust question
Unless you want to get into more detailed and involved treatments that take lots of time and the removal of parts etc, a quick fix is to remove the surface rust using a scotch pad (green washing up pad), then wipe the area with a cloth soaked in WD40 to blend it in. It will then take on more of black appearance than 'rust', and it won't rust again if kept indoors at normal temperature and humidity.
Edit, just noticed that PJL has posted a similar procedure above.
__________________
A digital radio is the latest thing, but a vintage wireless is forever.. |
15th Sep 2020, 5:44 pm | #19 |
Dekatron
Join Date: Apr 2012
Location: Wiltshire, UK.
Posts: 13,976
|
Re: Rust question
If you're storing radios/parts in an environment where there's a possible risk of future rust, it could be worth looking at "Vapor phase Corrosion Inhibitor" products - you've probably come across these in the form of brown, slightly-waxy-textured paper used in packaging for drills, bearings, knives etc.
https://en.wikipedia.org/wiki/Volati...sion_inhibitor Wrap your metal 'thing' in VCI paper, then over-wrap with cling-film! They didn't have cling-film during WWII but I've unwrapped several bits of 1940s US Military gear that's been protected by VCI paper and it's been in spectacularly-good condition. |
16th Sep 2020, 7:39 am | #20 |
Nonode
Join Date: Nov 2016
Location: Aberaeron, Ceredigion, Wales, UK.
Posts: 2,874
|
Re: Rust question
I remember a rust treatment that when applied to rust would turn a slightly blue in colour.
John |